The development of waterborne polyurethane (WPU) has been stimulated as an alternative to solvent-based polyurethanes due to low-VOC alternatives and reduced exposure to solvents. However, their relatively low mechanical performance and degradation have presented challenges in their wide application. Here, we developed environmentally-friendly bio polyol-based WPU nanocomposite dispersions and films, and presented the optimal process conditions for their manufacture. Additionally, the condition was established without using harmful catalysts or ethyl methyl ketone (MEK) during the polymerization. Moreover, regenerated cellulose nanoparticles (RCNs) were employed as natural chain-extenders in order to improve the biodegradability and mechanical performances of the nanocomposite films. The RCNs have a lower crystallinity compared to cellulose nanocrystals (CNCs), allowing them to possess high toughness without interfering with the elastomeric properties of polyurethane. The prepared CWPU/RCNs nanocomposite films exhibited high toughness of 58.8 ± 3 kgf∙mm and elongation at break of 240 ± 20%. In addition, depending on the molar ratio of NCO/OH, the polyurethane particle size is variously controlled from 70 to 230 nm, enabling to fabricate their dispersions with various transmittances. We believe that our findings not only open a meaningful path toward green elastomers with biodegradability but provides the design concept for bio-elastomers in order to develop industrial elastomers with mechanical and thermal properties.
Keywords: environmentally friendly; nanocomposite film; natural filler; regenerated cellulose; stretchable; waterborne polyurethane.