Astragalus is widely cultivated in China, and the residue of Astragalus particles (ARP) can be used as reinforcements in fused filament-fabricated (FFF) natural fiber/Poly(lactic acid)(PLA) biocomposites. To clarify the degradation behavior of such biocomposites, 3D-printed 11 wt% ARP/PLA samples were buried in soil, and the effects of soil burial duration on the physical appearance, weight, flexural properties, morphology, thermal stability, melting, and crystallization properties were investigated. At the same time, 3D-printed PLA was chosen as a reference. The results showed that, with prolonged soil burial, the transparency of PLA decreased (but not obviously), while the surface photographs of ARP/PLA became gray with some black spots and crevices; especially after 60 days, the color of the samples became extremely heterogeneous. After soil burial, the weight, flexural strength, and flexural modulus of the printed samples all reduced, and greater losses happened to ARP/PLA pieces than pure PLA. With an increase in soil burial time, the glass transition, cold crystallization, and melting temperatures, as well as the thermal stability of PLA and ARP/PLA samples, all increased gradually. Additionally, soil burial had a greater effect on the thermal properties of ARP/PLA. The results showed that the degradation behavior of ARP/PLA was more significantly affected by soil burial than the behavior of PLA. Additionally, ARP/PLA more easily degraded in soil than PLA.
Keywords: Astragalus residue powder; biocomposite; degradation; fused deposition modeling; poly(lactic acid); soil burial.