With the merits of low cost, environmental friendliness and rich resources, manganese dioxide is considered to be a promising cathode material for aqueous zinc-ion batteries (AZIBs). However, its low ion diffusion and structural instability greatly limit its practical application. Hence, we developed an ion pre-intercalation strategy based on a simple water bath method to grow in situ δ-MnO2 nanosheets on flexible carbon cloth substrate (MnO2), while pre-intercalated Na+ in the interlayer of δ-MnO2 nanosheets (Na-MnO2), which effectively enlarges the layer spacing and enhances the conductivity of Na-MnO2. The prepared Na-MnO2//Zn battery obtained a fairly high capacity of 251 mAh g-1 at a current density of 2 A g-1, a satisfactory cycle life (62.5% of its initial capacity after 500 cycles) and favorable rate capability (96 mAh g-1 at 8 A g-1). Furthermore, this study revealed that the pre-intercalation engineering of alkaline cations is an effective method to boost the properties of δ-MnO2 zinc storage and provides new insights into the construction of high energy density flexible electrodes.
Keywords: aqueous zinc-ion batteries; cathode; pre-intercalation; δ-MnO2.