Transparent conductive electrodes (TCE) obtained by the electrospinning method and gold covered were used as cathodes in the organic light-emitting diodes (OLEDs) to create double side-emission. The electro-active nanofibers of poly(methyl methacrylate) (PMMA) with diameters in the range of several hundreds of nanometers, were prepared through the electrospinning method. The nanofibers were coated with gold by sputtering deposition, maintaining optimal transparency and conductivity to increase the electroluminescence on both electrodes. Optical, structural, and electrical measurements of the as-prepared transparent electrodes have shown good transparency and higher electrical conductivity. In this study, two types of OLEDs consisting of indium tin oxide (ITO)/ poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT-PSS)/ Ir(III) complex (8-hydroxyquinolinat bis(2-phenylpyridyl) iridium-IrQ(ppy)2 20 wt% embedded in N, N'-Dicarbazolyl-4,4'-biphenyl (CBP) sandwich structure and either gold-covered PMMA electrospun nanoweb (OLED with electrospun cathode) were fabricated together with a similar structure containing thin film gold cathodes (OLED with thin film cathode). The luminance-current-voltage characteristics, the capacitance-voltage, and the electroluminescence properties of these OLEDs were investigated.
Keywords: double side-emission; electrospinning method; electrospun web cathodes; transparent conductive electrodes.