This study evaluates the performance of Polyethylene Terephthalate (PET)-modified hot mix asphalt. Aggregate, bitumen of grade 60/70 and crushed plastic bottle waste were utilized in this study. Polymer Modified Bitumen (PMB) was prepared using a high shear laboratory type mixer rotating at a speed of 1100 rpm with varying PET content of 2%, 4%, 6%, 8% and 10%, respectively. Overall, the results of preliminary tests suggested that bitumen hardened with the addition of PET. Following optimum bitumen content determination, various modified and controlled HMA samples were prepared as per wet and dry mixing techniques. This research presents an innovative technique to compare the performance of HMA prepared via dry and wet mixing techniques. Performance evaluation tests, which include the Moisture Susceptibility Test (ALDOT-361-88), Indirect Tensile Fatigue Test (ITFT-EN12697-24) and Marshall Stability and Flow Tests (AASHTO T245-90), were conducted on controlled and modified HMA samples. The dry mixing technique yielded better results in terms of resistance against fatigue cracking, stability and flow; however, the wet mixing technique yielded better results in terms of resistance against moisture damage. The addition of PET at more than 4% resulted in a decreased trend for fatigue, stability and flow due to the stiffer nature of PET. However, for the moisture susceptibility test optimum PET content was noted to be 6%. Polyethylene Terephthalate-modified HMA is found to be the economical solution for high volume road construction and maintenance, besides having other significant advantages such as increased sustainability and waste reduction.
Keywords: eco-friendly; fatigue life; flow; hot mix asphalt (HMA); moisture susceptibility; plastic bottles; polyethylene terephthalate (PET); polymer-modified bitumen (PMB); recycle; stability.