The most widely used material as a hole-transport layer (HTL) for effective normal perovskite solar cells (PSCs) is still 2,2',7,7'-Tetrakis[N, N-di(4-methoxyphenyl)amino]-9,9'-spirobifluorene (Spiro-OMeTAD), which requires heavy doping with the hydroscopic Lithium bis(trifluoromethanesulfonyl)imide (Li-ΤFSI). However, the long-term stability and performance of PCSs are frequently hampered by the residual insoluble dopants in the HTL, Li+ diffusion throughout the device, dopant by-products, and the hygroscopic nature of Li-TFSI. Due to the high cost of Spiro-OMeTAD, alternative efficient low-cost HTLs, such as octakis(4-methoxyphenyl)spiro[fluorene-9,9'-xanthene]-2,2',7,7'-tetraamine) (X60), have attracted attention. However, they require doping with Li-TFSI, and the devices develop the same Li-TFSI-derived problems. Here, we propose Li-free 1-Ethyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide (EMIM-TFSI) as an efficient p-type dopant of X60, resulting in a high-quality HTL with enhanced conductivity and deeper energy levels The optimized X60:EMIM-TFSI-enabled devices exhibit a higher efficiency of 21.85% and improved stability, compared to the Li-TFSI-doped X60 devices. The stability of the optimized EMIM-TFSI-doped PSCs is greatly improved, and after 1200 hr of storage under ambient conditions, the resulting PSCs maintain 85% of the initial PCE. These findings offer a fresh method for doping the cost effective X60 as the HTL with a Li-free alternative dopant for efficient, cheaper, and reliable planar PSCs.
Keywords: EMIM-TFSI; Li-TFSI; X60; hole transport layer; perovskite solar cell; stability.