Resin-based friction materials (RBFM) are widely used in the fields of automobiles, agriculture machinery and engineering machinery, and they are vital for safe and stable operation. In this paper, polymer ether ketone (PEEK) fibers were added to RBFM to enhance its tribological properties. Specimens were fabricated by wet granulation and hot-pressing. The relationship between intelligent reinforcement PEEK fibers and tribological behaviors was investigated by a JF150F-II constant-speed tester according to GB/T 5763-2008, and the worn surface morphology was observed using an EVO-18 scanning electron microscope. The results showed that PEEK fibers can efficiently enhance the tribological properties of RBFM. A specimen with 6 ωt% PEEK fibers obtained the optimal tribological performance, the fade ratio was -6.2%, which was much higher than that of the specimen without the addition of PEEK fibers, the recovery ratio was 108.59% and the wear rate was the lowest, which was 1.497 × 10-7 cm3/(Nm)-1. The reason for the enhancing tribological performance was that, on the one hand, PEEK fibers have a high strength and modulus which can enhance the specimens at lower temperatures; on the other hand, molten PEEK at high temperatures can also promote the formation of secondary plateaus, which are beneficial for friction. The results in this paper can lay a foundation for future studies on intelligent RBFM.
Keywords: friction materials; intelligent; polymer ether ketone fibers; secondary plateaus.