This work demonstrated a workable approach for the synthesis of a re-healing polyaniline-modified epoxy resin coating material via photopolymerization. The prepared coating material exhibited low water absorption, allowing it to be used as an anti-corrosion protective layer for carbon steel. First, graphene oxide (GO) was synthesized through the modified Hummers' method. It was then mixed with TiO2 to extend its light response range. The structural features of the coating material were identified using scanning electron microscopy (SEM), X ray diffraction (XRD), and Fourier-transform infrared spectroscopy (FT IR). The corrosion behavior of the coatings and the pure resin layer were tested by using electrochemical impedance spectroscopy (EIS) and the potentiodynamic polarization curve (Tafel). The presence of TiO2 reduced the corrosion potential (Ecorr) toward lower values in 3.5% NaCl at room temperature, which was due to the photocathode of titanium dioxide. The experimental results indicated that GO was successfully compounded with TiO2 and that GO effectively improved the light utilization capacity of TiO2. The experiments showed that the presence of local impurities or defects can reduce the band gap energy, resulting in a lower Eg for the 2GO:1TiO2 composite (2.95 eV) compared to that of TiO2 alone (3.37 eV). After applying visible light to the coating surface, the change in the Ecorr value of the V-composite coating was 993 mV and the value of Icorr decreased to 1.993 × 10-6 A/cm2. The calculated results showed that the protection efficiency of the D-composite and V-composite coatings on composite substrates was approximately 73.5 and 83.3%, respectively. More analyses revealed that under visible light, the coating had better corrosion resistance. This coating material is expected to be a candidate for carbon steel corrosion protection.
Keywords: anticorrosion coatings; graphene oxide; photopolymerization; polyaniline.