The current study aims to investigate a suitable adhesive for primary tooth enamel. Shear bond strength (SBS) of primary teeth and the length of resin protrusion were analyzed using one-way ANOVA with Bonferroni multiple comparison tests after etching with 35% H 3PO 4. SBS and marginal microleakage tests were conducted with Single Bond Universal (SBU)/Single Bond 2 (SB2) adhesives with or without pre-etching using a nonparametric Kruskal-Wallis test. Clinical investigations were performed to validate the adhesive for primary teeth restoration using Chi-square tests. Results showed that the SBS and length of resin protrusion increased significantly with the etching time. Teeth in the SBU with 35% H 3PO 4 pre-etching groups had higher bond strength and lower marginal microleakage than those in the SB2 groups. Mixed fractures were more common in the 35% H 3PO 4 etched 30 s + SB2/SBU groups. Clinical investigations showed significant differences between the two groups in cumulative retention rates at the 6-, 12- and 18-month follow-up evaluations, as well as in marginal adaptation, discoloration, and secondary caries at the 12- and 18-month follow-up assessments. Together, pre-etching primary teeth enamel for 30 s before SBU treatment improved clinical composite resin restoration, which can provide a suitable approach for restoration of primary teeth.
Keywords: Single Bond Universal; dentistry; marginal microleakage; primary teeth; restoration; shear bond strength.