This study aimed to evaluate the influence of temperature on torsional strength and angular deflection of two experimental NiTi rotary instruments manufactured from Blue and Gold thermal treatments and with identical cross-sections. A total of 40 experimental NiTi instruments 25.06 and with a triangular cross-section and manufactured from Blue and Gold thermal treatments were used (n=20). The torsional test was performed in the 3 mm from the tip of the instrument according to ISO 3630-1. The torsional test evaluated the torsional strength and angular deflection to failure at room temperature (21°C ± 1° C) and body temperature (36°C ±1°C). The fractured surface of each fragment was observed by using scanning electron microscopy (SEM). Data were analyzed using an unpaired t test for inter and intra-group comparison and the level of significance was set at 5%. The results showed that the body temperature did not affect the torsional strength and angular deflection of the instruments when compared with room temperature (P>0.05). However, at body temperature, the Blue NiTi instruments presented significantly lower angular deflection in comparison with Gold NiTi instruments (P<0.05). There was no significant difference regarding the torsional strength of the instruments at body temperature (P>0.05). The temperature did not affect the torsional strength of the instruments manufactured from Blue and Gold technology. However, the Blue NiTi instruments presented significantly lower angular deflection than Gold instruments at 36°C temperature.