Temperature is a fundamental physical quantity important to the physical and biological sciences. Measurement of temperature within an optically inaccessible three-dimensional (3D) volume at microscale resolution is currently limited. Thermal magnetic particle imaging (T-MPI), a temperature variant of magnetic particle imaging (MPI), hopes to solve this deficiency. For this thermometry technique, magnetic nano-objects (MNOs) with strong temperature-dependent magnetization (thermosensitivity) around the temperature of interest are required; here, we focus between 200 K and 310 K. We demonstrate that thermosensitivity can be amplified in MNOs consisting of ferrimagnetic (FiM) iron oxide (ferrite) and antiferromagnetic (AFM) cobalt oxide (CoO) through interface effects. The FiM/AFM MNOs are characterized by X-ray diffraction (XRD), (scanning) transmission electron microscopy (STEM/TEM), dynamic light scattering (DLS), and Raman spectroscopy. Thermosensitivity is evaluated and quantified by temperature-dependent magnetic measurements. The FiM/AFM exchange coupling is confirmed by field-cooled (FC) hysteresis loops measured at 100 K. Magnetic particle spectroscopy (MPS) measurements were performed at room temperature to evaluate the MNOs MPI response. This initial study shows that FiM/AFM interfacial magnetic coupling is a viable method to increase thermosensitivity in MNOs for T-MPI.
Keywords: FiM/AFM exchange coupling; colloidal synthesis; magnetic nano-objects; thermal magnetic particle imaging; thermosensitivity.