In this study, the mechanical properties of basalt/ramie/polyester hybrid composite laminates were investigated. A matrix of 45% polyester was used, as it has good bonding properties between fibers. The composite laminates were fabricated using a hand layup technique, with seven layers stacked in different sequences and impregnated in the polyester matrix to create a hybrid configuration. Tensile, flexural, impact, compression, and hardness tests were conducted according to ASTM standards for mechanical characterization. The results showed that the overall stacking sequence of sample number seven (BRBRBRB) had the highest tensile strength at 120 MPa, impact energy at 8 J, flexural strength at 115 MPa, compression strength at 70 MPa, and hardness of 77. Natural fiber-reinforced composites are being used in current automotive industry applications, such as in electric vehicles.
Keywords: SEM; flexural; hybrid composite; impact and hardness; microstructure analysis; tensile.