Background: The suture-tendon interface often constitutes the point of failure in tendon suture repair. In the present study, we investigated the mechanical benefit of coating the suture with a cross-linking agent to strengthen the nearby tissue after suture placement in human tendons and we assessed the biological implications regarding tendon cell survival in-vitro.
Methods: Freshly harvested human biceps long head tendons were randomly allocated to control (n = 17) or intervention (n = 19) group. According to the assigned group, either an untreated or a genipin-coated suture was inserted into the tendon. 24 h after suturing, mechanical testing composed of cyclic and ramp-to-failure loading was performed. Additionally, 11 freshly harvested tendons were used for short-term in vitro cell viability assessment in response to genipin-loaded suture placement. These specimens were analyzed in a paired-sample setting as stained histological sections using combined fluorescent/light microscopy.
Findings: Tendons stitched with a genipin-coated suture sustained higher forces to failure. Cyclic and ultimate displacement of the tendon-suture construct remained unaltered by the local tissue crosslinking. Tissue crosslinking resulted in significant cytotoxicity in the direct vicinity of the suture (<3 mm). At larger distances from the suture, however, no difference in cell viability between the test and the control group was discernable.
Interpretation: The repair strength of a tendon-suture construct can be augmented by loading the suture with genipin. At this mechanically relevant dosage, crosslinking-induced cell death is confined to a radius of <3 mm from the suture in the short-term in-vitro setting. These promising results warrant further examination in-vivo.
Keywords: Cell viability; Collagen crosslinking; Mechanical testing; Soft tissue repair; Suture; Tendon.