Coordination of clinically employed bisphosphonate, risedronate (RISE), to bioactive metals, Ca2+, Mg2+, and Zn2+, allowed the formation of bisphosphonate-based coordination complexes (BPCCs). Three RISE-based BPCCs, RISE-Ca, RISE-Mg, and RISE-Zn, were produced, and their structures were elucidated by single crystal X-ray diffraction. Interestingly, the addition of an auxiliary ligand, etidronic acid (HEDP), resulted in the recrystallized protonated form of the ligand, H-RISE. The pH-dependent structural stability of the RISE-based BPCCs was measured by means of dissolution profiles under neutral and acidic simulated physiological conditions (PBS and FaSSGF, respectively). In comparison to RISE (Actonel), the complexes showed a lower equilibrium solubility (∼70-85% in 18-24 h) in PBS, while a higher equilibrium solubility (∼100% in 3 h) in acidic media. The results point to the capacity to release this BP in a pH-dependent manner from the RISE-based BPCCs. Subsequently, the particle size of RISE-Ca was reduced, from 300 μm to ∼350 d.nm, employing the phase inversion temperature (PIT)-nanoemulsion method, resulting in nano-Ca@RISE. Aggregation measurements of nano-Ca@RISE in 1% fetal bovine serum (FBS):H2O was monitored after 24, 48, and 72 h to study the particle size longevity in physiological media, showing that the suspended material has the potential to maintain its particle size over time. Furthermore, binding assays were performed to determine the potential binding of nano-Ca@RISE to the bone, where results show higher binding (∼1.7×) for the material to hydroxyapatite (HA, 30%) when compared to RISE (17%) in 1 d. The cytotoxicity effects of nano-Ca@RISE were compared to those of RISE against the human breast cancer MDA-MB-231 and normal osteoblast-like hFOB 1.19 cell lines by dose-response curves and relative cell viability assays in an in vitro setting. The results demonstrate that nano-Ca@RISE significantly decreases the viability of MDA-MB-231 with high specificity, at concentrations ∼2-3× lower than the ones reported employing other third-generation BPs. This is supported by the fact that when normal osteoblast cells (hFOB 1.19), which are part of the tissue microenvironment at metastatic sites, were treated with nano-Ca@RISE no significant decrease in viability was observed. This study expands on the therapeutic potential of RISE beyond its antiresorptive activity through the design of BPCCs, specifically nano-Ca@RISE, that bind to the bone and degrade in a pH-dependent manner under acidic conditions.
Keywords: binding; bisphosphonates; coordination complexes; osteolytic metastases; risedronate.