This study illustrated the potential applications of thermoresponsive poly(N-isopropylacrylamide) (PNIPAm) grafted nylon membranes with different grafting yields and grafting architecture. The thermoresponsive gating performance at temperatures below and above the lower critical solution temperature (LCST) of PNIPAm (32 °C) were demonstrated. The linear PNIPAm-grafted nylon membrane exhibited a sharp response over the temperature range 20-40 °C. The grafting yield of 25.5% and 21.9%, for linear and crosslinked PNIPAm respectively, exhibited highest thermoresponsive gating function for water flux and had a stable and repeatable "open-closed" switching function over 5 cycle operations. An excellent oil/water separation was obtained at T < 32 °C, at which the hydrophilic behavior was observed. The linear PNIPAm-grafted nylon membrane with 35% grafting yield had the highest separation efficiency of 99.7%, while PNIPAm structures were found to be independent of the separation efficiency. In addition, the membranes with thermoresponsive gas permeability were successfully achieved. The O2 and CO2 transmission rates through the PNIPAm-grafted nylon membranes decreased when the grafting yield increased, showing the better gas barrier property. The permeability ratio of CO2 to O2 transmission rates of both PNIPAm architectures at 25 °C and 35 °C were around 0.85 for low grafting yields, and approximately 1 for high grafting yields. Ultimately, this study demonstrated the possibility of using these thermoresponsive smart membranes in various applications.
Keywords: gas permeability; nylon membrane; oil-water separation; poly(N-isopropylacrylamide); smart membrane; thermoresponsive polymer; water filtration.