Carbon Quantum dot (CQDs) is one of the newest materials in carbon-based nanomaterials. It is pertinent to study the synthesis and the application of these carbon dots. Here we have studied the effect of precursor on the optical, morphological, and photocatalytic properties of CQDs. We have synthesized CQDs using pyrolysis method using the precursors citric acid, urea, polyethyleneimine. We have synthesized two samples: CQD-S1; synthesized using urea and polyethyleneimine, and CQD-S2; synthesized using citric acid and polyethyleneimine. In optical properties study two distinct peaks have been obtained at 243 nm and 345 nm for CQD-S1, and at 265 nm and 335 nm for CQD-S2. In fluorescence study, the maximum emission was found at excitation wavelength of 340 nm for CQD-S1 and at excitation wavelength of 350 nm for CQD-S2. In morphological studies, Transmission Electron Microscope (TEM) revealed particle size of sample CQD-S1 and CQD-S2 were 1.91 nm and 1.61 nm, respectively. EDX confirmed the elemental composition in both samples. The rhodamine B (RhB) dye degradation percentages in dark and under visible and UV light were found to 6, 13, and 98.4% respectively for CQD-S1. Similarly, dye degradation for CQD-S2 were 7, 11, and 99.63%, respectively. Effective degradation of photocatalysis performed under UV-light within 100 min using mineralization process.
Keywords: Carbon Quantum dots; Citric acid; Photocatalysis; Polyethyleneimine; Rhodamine B; Urea.
© 2023. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.