A New Class of Proton Conductors with Dramatically Enhanced Stability and High Conductivity for Reversible Solid Oxide Cells

Abstract

Reversible solid oxide cells based on proton conductors (P-ReSOCs) have potential to be the most efficient and low-cost option for large-scale energy storage and power generation, holding promise as an enabler for the implementation of intermittent renewable energy technologies and the widespread utilization of hydrogen. Here, the rational design of a new class of hexavalent Mo/W-doped proton-conducting electrolytes with excellent durability while maintaining high conductivity is reported. Specifically, BaMo(W)_0.03 Ce_0.71 Yb_0.26 O_3-δ exhibits dramatically enhanced chemical stability against high concentrations of steam and carbon dioxide than the state-of-the-art electrolyte materials while retaining similar ionic conductivity. In addition, P-ReSOCs based on BaW_0.03 Ce_0.71 Yb_0.26 O_3-δ demonstrate high peak power densities of 1.54, 1.03, 0.72, and 0.48 W cm^-2 at 650, 600, 550, and 500 °C, respectively, in the fuel cell mode. During steam electrolysis, a high current density of 2.28 A cm^-2 is achieved at a cell voltage of 1.3 V at 600 °C, and the electrolysis cell can operate stably with no noticeable degradation when exposed to high humidity of 30% H₂ O at -0.5 A cm^-2 and 600 °C for over 300 h. Overall, this work demonstrates the promise of donor doping for obtaining proton conductors with both high conductivity and chemical stability for P-ReSOCs.

Keywords: donor doping; high ionic conductivity; proton-conducting electrolytes; reversible solid oxide cells; water tolerance.