It is of great significance to develop green, sustainable additives to improve the thermal stability and flame retardancy of biopolymers. In this work, a synergistic modification of P/N elements to bamboo biochar (mBC) was successfully achieved by grafting a reaction of phytic acid and urea with preoxidized bamboo biochar. Fourier transform infrared spectroscopy, X-ray diffraction, nuclear magnetic resonance and scanning electron microscope determinations of the mBC demonstrated a successive grafting of phytic acid and urea to the originally porous surface. The ground mBC was blended with polylactic acid (PLA) to prepare mBC/PLA composites by extrusion and hot pressing. Mechanical strength studies showed a compromise in rigidity, which might originate from the mBC overdose and its limited miscibility with the resin. The thermogravimetric results supported the fact that the enhancement of thermal stability and flame retardancy of the composites with the mBC dosage, which showed that the mBC dosage in the PLA composites was not only lower than that of the conventional flame retardants, but also outperformed the counterparts using BC modified by inorganic phosphoric acid and urea. The mBC was prone to accelerate the earlier decomposition of the composites (30 °C lower in decomposition) and generate a continuous, dense residual carbon layer, which provides an effective shield resisting the mass and heat transfer between the combustion area and the underlying composite matrix. Only 10 wt% of mBC dosage could achieve a V-0 rating (UL94) for the composite, with a higher limiting oxygen index up to 28.3% compared to 20.7% for that of the virgin PLA; the cone colorimetric results also suggested that the flame retardancy had been greatly improved for all composites. In this work, biobased P-/N-containing bamboo biochar would be expected as a nontoxic biochar-based flame retardant that serves as green filler in polymer composites.
Keywords: bamboo biochar; co-modification; flame retardancy; oxidation; polylactic acid(PLA).