Vitrified bond cubic boron nitride (CBN) grinding wheel specimens with controllable porosity were prepared by regulating the pore former dextrin content and varying the forming pressure, and the performance of the grinding camshaft was studied. The porosity of the specimens increases with the increase in dextrin content, and decreases first and then increases with the increase in the forming pressure. The grinding experiments show that the dextrin content is negatively correlated with the grinding force and grinding temperature, while the grinding force and grinding temperature of the specimens increase and then decrease with the increase in the forming pressure. When we observe and measure the grinding surface of the specimen and workpiece, we see that the surface roughness of the specimen after grinding is smaller than that before grinding. In addition, the greater the porosity of the specimen, the rougher the surface of the workpiece after grinding.
Keywords: controllable porosity; grinding force; grinding temperature; surface roughness; vitrified bond CBN grinding wheel specimens.