Single-walled carbon nanotube buckypapers (SWCNT-bps) coated with a metal-organic framework ZIF-8 layer were used as supports for the preparation of Pebax® 3533 TFC membranes by both phase inversion and spin coating techniques. Upon proper characterization of the materials by X-ray diffraction, IR spectroscopy, thermogravimetry and electron microscopy, the obtained membranes were tested in gas separation experiments with a 15:85 CO2/N2 mixture. These experiments proved that the ZIF-8 layer prevented from the penetration of the polymer selective film into the SWCNT-bp support, giving rise to a highly permeable selective membrane. The optimum membrane was achieved by the spin-coating method, with better permeation results than that prepared by the phase inversion method, obtaining a CO2 permeance of 566 GPU together with a CO2/N2 selectivity of 20.9.
Keywords: CO2 capture; ZIF-8; buckypaper; gas separation; metal–organic framework; single-walled carbon nanotube.