High-activity spherical TaNbTiZr refractory high-entropy alloy (REHA) powders were successfully prepared by electrode induction melting gas atomization (EIGA) and plasma rotating electrode process (PREP) methods. Both the EIGAed and PREPed TaNbTiZr RHEA powders have a single-phase body-centered cubic (BCC) structure and low oxygen content. Compared with the EIGAed powders, the PREPed powders exhibit higher sphericity and smoother surface, but larger particle size. The average particle sizes of the EIGAed and PREPed powders are 51.8 and 65.9 μm, respectively. In addition, both the coarse EIGAed and PREPed powders have dendritic structure, and the dendrite size of the EIGAed powders is larger than that of the PREPed powders. Theoretical calculation indicates that the cooling rate of the PREPed powders is one order of magnitude higher than that of the EIGAed powders during the solidification process, and the dendritic structure has more time to grow during EIGA, which is the main reason for the coarser dendrite size of the EIGAed powders.
Keywords: EIGA; PREP; TaNbTiZr; refractory high-entropy alloy; spherical powder.