Fabrication of Superhydrophobic Coating Based on Waterborne Silicone-Modified Polyurethane Dispersion and Silica Nanoparticles

Polymers (Basel). 2022 Dec 21;15(1):22. doi: 10.3390/polym15010022.

Abstract

In this work, eco-friendly superhydrophobic coatings were prepared by dispersing hydrophobic silica nanoparticles and a waterborne silicone-modified polyurethane dispersion into an ethanol solution, which was free of fluorine and volatile toxic solvents. The effects of the silica content on the hydrophobicity and scratch resistance of the hydrophobic surfaces were investigated by WCA measurements and a sandpaper abrasion test, respectively. The experimental results indicated that when the silica content exceeded 30% by mass, the silica/silicone-modified polyurethane coatings had superhydrophobicity. Meanwhile, the superhydrophobic coatings with a silica content of 30% by mass simultaneously had the optimal mechanical stability. We studied the morphology and roughness of the hydrophobic surfaces with different silica content and attempted to briefly explain the influence mechanism of silica content. Furthermore, anti-icing and oil-water separation experiments were carried out on the superhydrophobic coatings, which exhibited good anti-icing performance and high separation efficiency. The eco-friendly superhydrophobic coating is expected to be applied in the fields of oil-water separation, anti-icing, and self-cleaning, etc.

Keywords: eco-friendly; nano-composites; superhydrophobic coating.