Selective Laser Melting (SLM) is an emerging Additive Manufacturing (AM) technique for the on-demand fabrication of metal parts. The mechanical properties of Selectively Laser Melted (SLMed) parts are sensitive to oxygen concentration within the SLM build chamber due to the formation of oxides, which may lead to various negative consequences. As such, this work explores the influence of SLM atmospheric Oxygen Content (OC) on the macroscopic mechanical properties of SLMed AlSi10Mg bulk material and Triply Periodic Minimal Surface (TPMS) lattices namely primitive, gyroid, and diamond. Standard quasi-static tensile and crushing tests were conducted to evaluate the bulk properties of AlSi10Mg and the compressive metrics of TPMS-lattices. Two oxygen concentrations of 100 ppm and 1000 were used during the SLM fabrication of the experimental specimens. The tensile test data revealed a small influence of the oxygen content on the bulk properties. The low oxygen concentration improved the elongation while slightly reduced the ultimate tensile strength and yield stress. Similarly, the influence of the oxygen content on the compressive responses of TPMS-lattices was generally limited and primarily depended on their geometrical configuration. This study elucidates the role of SLM atmospheric oxygen content on the macroscopic behaviour of SLMed AlSi10Mg parts.
Keywords: AlSi10Mg; TPMS; additive manufacturing; aluminium alloys; oxygen content; selective laser melting.