Reducing the negative environmental impact of a widely spread building material such as concrete is possible by decreasing the amount of cement in this composite material, especially when specific waste is included as a substitution for the binder. Another important environmental issue is accumulated aquaculture waste. This work justifies the possibility of achieving modified concrete with improved properties based on sea mussel shell powder (MSP). An improved environmentally friendly concrete was obtained and modified with MSP as a result of experimental studies. The dosage of MSP in the amount of 6% instead of part of the cement turned out to be optimal and most effective. Because of the modification, it was possible to increase the strength properties: the increments were up to 12% for the compressive strength (CS), up to 13% for the axial CS, up to 14% for the tensile strength (TS) in bending, and up to 12% for the axial TS. The ultimate strains under axial compression and tension decreased to 9% and 12%, respectively, and the elastic modulus increased to 15%. SEM analysis showed a more integral microstructure without voids and cracks in this composite with a modifier content of 6% compared with the sample of the ordinary composition. Economic efficiency is expressed in reducing the total cost of new concrete compared to traditional ones by about 17% and the cost of building construction by up to 15% due to a decrease in the percentage of defects.
Keywords: concrete microstructure; deformation characteristics; modified concrete; mussel shell powder; strength characteristics.