Evolution of pore structure and radon exhalation characterization of porous media grouting

Xinchao Zheng; Qiang Sun; Xudong Jing; Duoxing Yang; Hailiang Jia

doi:10.1016/j.scitotenv.2022.161352

Evolution of pore structure and radon exhalation characterization of porous media grouting

Sci Total Environ. 2023 Mar 20:865:161352. doi: 10.1016/j.scitotenv.2022.161352. Epub 2022 Dec 31.

Authors

Xinchao Zheng¹, Qiang Sun², Xudong Jing³, Duoxing Yang⁴, Hailiang Jia⁵

Affiliations

¹ College of Geology and Environment, Xi'an University of Science and Technology, Xi'an, Shaanxi 710054, China. Electronic address: zhengxinchao@stu.xust.edu.cn.
² College of Geology and Environment, Xi'an University of Science and Technology, Xi'an, Shaanxi 710054, China; Shaanxi Provincial Key Laboratory of Geological Support for Coal Green Exploitation, 710054, China; Key Laboratory of Coal Resources Exploration and Comprehensive Utilization, Ministry of Land and Resources, China. Electronic address: sunqiang04@cumt.edu.cn.
³ College of Geology and Environment, Xi'an University of Science and Technology, Xi'an, Shaanxi 710054, China. Electronic address: 20209226082@stu.xust.edu.cn.
⁴ National Institute of Natural Hazards, Ministry of Emergency Management of China, Beijing 100085, China. Electronic address: dxyang@ninhm.ac.cn.
⁵ College of Architecture and Civil Engineering, Xi'an University of Science and Technology, Xi'an, Shaanxi 710054, China. Electronic address: hailiang.jia@xust.edu.cn.

PMID: 36596422
DOI: 10.1016/j.scitotenv.2022.161352

Abstract

Cracks and pores are considered as major sources of radon. Cement is widely used as a grouting material in mines, tunnels, and other projects for reinforcement, seepage prevention, and water plugging. This paper mainly experimentally studied the correlation between the radon exhalation rate of the porous medium after grouting and the sand grain diameter, grouting pressure, and slurry water-cement ratio. The pore characteristics of the samples before and after grouting were also studied based on the low field nuclear magnetic resonance (LF-NMR). The findings of the study show that the porosity of samples increases after the superfine cement solidification with an increase in the water-cement ratio, and the radon exhalation rate is proportional to porosity, the radon exhalation rate increases by 0.0005 Bq·m-2/s at W/C = 1.5, and by 0.0017 Bq·m^-2/s at W/C = 2 increases, in comparison to the W/C = 1.The radon exhalation rate of porous media gradually increased after grouting in response to an increase in grouting pressure and the water-cement ratio. The radon exhalation rate of the porous media with larger pores was relatively higher and exhibited a positive correlation with the volume of micropores in porous media，the correlations of coarse, medium and fine media are 0.815, 0.826, and 0.859. The change in pore structure has an influence on radon exhalation. Although grouting changes the pore structure and reduces the connectivity between internal pores, the micropores generated after cement slurry solidification improves the radon exhalation rate by providing new channels, When the water-cement ratio is 1.5 and the grouting pressure is 1.5 MPa, the radon exhalation rate of porous media is 0.00273 Bq·m^-2/s. The research results serve as a reference basis for the evaluation of the impact of rock masses on grouting reinforcement and pore sealing.

Keywords: Grouting; Pore structure; Porous media; Radon exhalation rate; Superfine cement.