Metal-organic frameworks-derived In2O3/ZnO porous hollow nanocages for highly sensitive H2S gas sensor

Abstract

The detection of hydrogen sulfide (H₂S) is critical because of its potential harm and widespread presence in the oil and gas sectors. The zeolitic imidazolate framework-8 (ZIF-8) derived ZnO nanostructures manufactured as gas sensors have exceptional sensitivity and selectivity for H₂S gas. In/Zn-ZIF-8 template material was synthesized by a simple one-step co-precipitation method followed by thermal annealing in air. The heat treatment resulted in In₂O₃/ZnO nanostructures with mixed heterostructures. The crystal structure (XRD), morphology (SEM/TEM), chemical state (XPS), surface area (BET), etc were investigated to ascertain the nature of the as-prepared material. SEM imagery revealed that the as-prepared In₂O₃/ZnO sensitive material had a microstructure of porous hollow nanocages with an average particle size of about 200 nm, which is beneficial to the diffusion and adsorption of gas molecules. The gas sensing performance test results of the In₂O₃/ZnO hollow nanocages show that their response to H₂S gas is significantly improved 67.5 @50 ppm H₂S (about 11 times that of pure ZnO nanocages) at an optimal temperature of 200 °C, better selectivity, lower theoretical detection limit and good linearity between gas concentration and response values. The enhanced gas sensing feat to H₂S gas is mainly attributed to the formation of n-n heterojunction and the wide surface area of the newly formed In₂O₃/ZnO porous hollow nanocages.

Keywords: Gas sensors; H(2)S; In(2)O(3); Nanocages; ZnO.