In this work, a low-power memristor based on vertically stacked two-dimensional (2D) layered materials, achieved by plasma-assisted vapor reaction, as the switching material, with which the copper and gold metals as electrodes featured by reversible polymorphous phase changes from a conducting 1T-phase to a semiconducting 2H-one once copper cations interacted between vertical lamellar layers and vice versa, was demonstrated. Here, molybdenum diselenide was chosen as the switching material, and the reversible polymorphous phase changes activated by the intercalation of Cu cations were confirmed by pseudo-operando Raman scattering, transmission electron microscopy, and scanning photoelectron microscopy under high and low resistance states, respectively. The switching can be activated at about ±1 V with critical currents less than 10 μA with an on/off ratio approaching 100 after 100 cycles and low power consumption of ∼0.1 microwatt as well as linear weight updates controlled by the amount of intercalation. The work provides alternative feasibility of reversible and all-solid-state metal interactions, which benefits monolithic integrations of 2D materials into operative electronic circuits.
Keywords: intercalation; memristor; molybdenum diselenide; polymorphous phase; vertically aligned lamellar structure.