This work presents the results of an experimental investigation of the mechanical properties of polyetheretherketone (PEEK) specimens additively manufactured (AM) by using fused filament fabrication with different printing parameters and subjected to postprocessing heat treatment. Standard and compact tension samples were manufactured with a different infill angle using 0.4 mm and 0.6 mm nozzle diameters. Some of the samples were subjected to heat treatment at 220 °C after manufacturing. Tensile tests were conducted to determine the values of elastic modulus, tensile strength, as well as mode-I fracture toughness and critical strain energy release rate. Tensile properties of single-thread and as-delivered filaments were also studied. It was concluded that heat treatment significantly improved the elastic properties, tensile strength and fracture toughness of the AM PEEK samples: the fracture resistance increased by 33 to 45% depending on the stacking order, while the tensile strength increased by some 45-65%, with the elasticity modulus grown by up to 20%. Strain fields induced in specimens by crack propagation were captured with a digital image correlation technique and compared with results of numerical simulations implemented with the extended finite-element method (XFEM). Conclusions on the optimal parameters of 3D printing of PEEK were made.
Keywords: PEEK; biocompatible polymers; fracture toughness; heat treatment; infill orientation; manufacturing parameters; mechanical properties.