In this study, the influence of TiO2 pigment filler modified with spherosilicate derivatives on the processes and thermomechanical properties of composites based on PLA was investigated. Rheological tests (MFR) were carried out, on the basis of which it was found that the addition of organosilicon compounds has a plasticizing effect on the polymer-filler systems. TGA and DSC analysis were performed. The analysis of the contact angle showed that 1.5% of the additives had an influence on the superhydrophobic properties of TiO2 (above 135°), and a slight improvement of this parameter was also observed for composites containing the modified pigment. Microscopic analysis and mechanical tests (tensile strength, impact strength and flexural strength tests) were carried out as well. It has been observed that the addition of certain derivatives adversely affects the dispersion of the filler, thus a slight improvement in mechanical properties is observed. For modifiers that do not affect filler agglomeration, a plasticizing effect on the composite is observed.
Keywords: 3D printing; PLA; POSS; additive manufacturing; polylactide; silsesquioxane; titanium dioxide.