Objectives: To evaluate the effect of thickness on color and translucency of a multi-color polymer-infiltrated ceramic-network (PICN) material.
Methods: Specimens of 0.5, 1.0, 1.5 mm thicknesses were obtained by sectioning VITA ENAMIC® multiColor (E-MC) High Translucent CAD-CAM blocks (1M1-HT, 1M2-HT, 2M2-HT, 3M2-HT, and 4M2-HT). Spectral reflectance and color coordinates were measured on white and black backgrounds using a spectroradiometer, CIE D65 illuminant and CIE 45°/0° geometry. CIEDE2000 color and translucency differences (ΔE00 and ΔTP00 ) between thicknesses and adjacent layers were evaluated using their respective 50:50% perceptibility and acceptability thresholds (PT00 and AT00 ).
Results: In general, ΔE00 between thicknesses for all shades and layers were above AT00 in general. Chroma decreased from cervical to incisal layers with statistically significant differences (p < 0.05), and ΔE00 between sequential layers were above PT00 , for all shades and thicknesses. TP00 decreased from 0.5 to 1.5 mm and increased from cervical to incisal layers for all shades with statically significant translucency differences (p < 0.05). In general, for all thicknesses, TPT00 < ΔTP00 < TAT00 for sequential layers.
Conclusions: The gradient in color and translucency of E-MC PICN material was influenced by the thickness of the CAD-CAM block. In addition, color and TP transition values between the layers depends on the thickness and shade.
Clinical significance: The effect of thickness must be taken into account by dental technicians and dentists when CAD-CAM multicolor PICN materials are used.
Keywords: PICN material; color; thickness; translucency parameter; visual thresholds.