Non-preheating fabricated semitransparent quasi-2D perovskite solar cells

Wenjie Luo; Qingqing Qiu; Rui Liu; Yue Yu; Qiaofeng Wu; Jin Peng; Xudong Cai; Jian Yu; Xin Chen; Hua Yu

doi:10.1039/d2cc05797b

Non-preheating fabricated semitransparent quasi-2D perovskite solar cells

Chem Commun (Camb). 2023 Jan 5;59(4):430-433. doi: 10.1039/d2cc05797b.

Authors

Wenjie Luo¹, Qingqing Qiu¹, Rui Liu¹, Yue Yu¹, Qiaofeng Wu¹, Jin Peng¹, Xudong Cai¹, Jian Yu¹, Xin Chen², Hua Yu¹

Affiliations

¹ School of New Energy and Materials, Southwest Petroleum University, Chengdu, 610500, P. R. China. 201899010017@swpu.edu.cn.
² Center for Computational Chemistry and Molecular Simulation, College of Chemistry and Chemical Engineering, Southwest Petroleum University, Chengdu, 610500, China.

PMID: 36515140
DOI: 10.1039/d2cc05797b

Abstract

Although the hot-casting (HC) method can obtain efficient quasi-2D perovskite solar cells, this method cannot effectively control the uniformity of the thin film, and the high preheating substrate temperature will also form low n perovskite phases (n = 2) at the interface, which is not conducive to the transport of carriers. Semitransparent solar cells have great application prospects in building-integrated photovoltaic and tandem devices. Herein, a non-preheating (NP) film-casting method is proposed to realize a highly uniform and phase controllable quasi-2D perovskite film (BA₂MA₃Pb₄I₁₃, BA⁺:C₄H₁₁NH₃⁺, MA⁺:CH₃NH₃⁺). As a result, the NP-processed film gets the highest light utilization efficiency (LUE = 4.01%) for semitransparent quasi-2D perovskite solar cells (ST-Quasi-2D-PSCs) with power conversion efficiency (PCE) of 9.60%, average visible transmittance (AVT) of 41.73%, good bifaciality factor, high LUE in low light intensity and good stability.