The use of thermal insulated decorative panel materials with low thermal conductivity and high flame retardance is a key step toward energy-saving buildings. However, traditional thermal insulation materials are always highly conductive and inflammable, which restricts their application for new buildings. This study aims to prepare the non-combustible, cement-based EPS mixtures with thermal conductivity lower than 0.045 and density less than 140 kg/m3 and characterize it with mechanical, thermal, and flame retardant properties. The effect of particle size, Silica coated and content of EPS on the physical, mechanical, thermal, and combustion performance are conducted in this paper. The comprehensive indoor tests including density, water absorbing, softening coefficient, compressive strength, tensile strength, moisture susceptibility, thermal conductivity, and scanning electron microscopy (SEM) along with combustion performance are reported to evaluate the effects of several variables on the investigated cement-based nonflammable EPS (CEPS)mixtures. The results show that small and gradation EPS particles significantly improve the comprehensive performance of mixtures. In addition, Silica coated ESP significantly improve the flame retardance of mixtures while reduce the mechanical characteristics slightly. These results contribute to the selection of appropriate materials to enhance the thermal insulation, flame retardance and mechanical properties of CEPS.
Keywords: expanded polystyrene (EPS); external thermal insulation composite; flame retardance; mechanical characterization; thermal conductivity.