The emission of semi-volatile heavy metals during the thermal utilization of various fuels has been a huge threat to the environment. In this study, the montmorillonite modified by thermal treatment and hydrochloric acid activation was evaluated for the PbCl2 adsorption performance. The optimum adsorption temperature of sorbents increased with the thermal treatment temperature (<500 °C) for the increased amount of reactive sites caused by the removal of interlayer water and hydroxyl, while a higher treatment temperature will collapse the lamellar structure of montmorillonite and greatly inhibit the PbCl2 adsorption. Besides, the hydrochloric acid activation can help inhibit the melting of sorbents during the adsorption process by removing the impurities and promote the PbCl2 vapor to contact with more reactive sites at higher temperatures. By comparing different sorbents, montmorillonite was found to exhibit better adsorption performance at 600-700 °C, while the sorbent thermal-treated at 500 °C and then acid-activated got the highest adsorption efficiency at 900 °C, which was 17.83% higher than that of montmorillonite. This study provided an environmental-friendly modification method to capture more heavy metals at high-temperature conditions, which can be partly realized by the recycling of montmorillonite used for the removal of normal gas pollutants in lower temperatures conditions or acid wastewater treatment.
Keywords: Acid activation; High temperature; Montmorillonite; PbCl(2) adsorption; Thermal treatment.
Copyright © 2022. Published by Elsevier Ltd.