In order to make full use of crop waste stalk, corn-stalk cellulose (CSC) was extracted by acid-base method and used as modifier of epoxy resin (E51) to prepare the self-extracted corn-stalk cellulose/epoxy resin composites (CSCEC). Differential scanning calorimeter (DSC), thermogravimetry (TG) analysis, dynamic mechanical analysis (DMA), morphology analysis by scanning electron microscope (SEM), the mechanical properties by electronic universal testing machine and impact testing machine were used for characterization and analysis. The experimental results showed that when the CSC content was 20 wt%, the impact strength of the composite was 2.50 kJ/m2, which was 127.2% higher than that of pure epoxy resin. When the CSC content was 20 wt%, the Tg of epoxy resin obtained by DMA was the lowest, 167.4 °C, which decreased by 11.3 °C compared with that of pure epoxy resin. The SEM result showed that the fracture surface of the composite became obviously rough and had of obvious folds, which was a ductile fracture. These results indicated that the addition of CSC could toughen the epoxy resin.
© 2022. The Author(s).