Aluminum nanoparticles attract scientific interest as a promising low-cost material with strong plasmon resonance in the ultraviolet region, which can be used in various fields of photonics. In this paper, for the first time, ultraviolet luminescence of zinc oxide nanoparticles in colloid solutions and nanostructure films in the presence of plasmonic aluminum nanoparticles 60 nm in size with a metal core and an aluminum oxide shell were studied. Mixture colloids of ZnO and Al nanoparticles in isopropyl alcohol solution with concentrations from 0.022 to 0.44 g/L and 0.057 to 0.00285 g/L, correspondingly, were investigated. The enhancement of up to 300% of ZnO emission at 377 nm in colloids mixtures with metal nanoparticles due to formation of Al-ZnO complex agglomerates was achieved. Plasmon nanostructures with different configurations of layers, such as Al on the surface of ZnO, ZnO on Al, sandwich-like structure and samples prepared from a colloidal mixture of ZnO and Al nanoparticles, were fabricated by microplotter printing. We demonstrated that photoluminescence can be boosted 2.4-fold in nanostructures prepared from a colloidal mixture of ZnO and Al nanoparticles, whereas the sandwich-like structure gave only 1.1 times the amplification of luminescence. Calculated theoretical models of photoluminescence enhancement of ideal and weak emitters near aluminum nanoparticles of different sizes showed comparable results with the obtained experimental data.
Keywords: aluminum nanoparticles; colloidal mixture; microplotter printing; numerical modeling; plasmon enhanced luminescence; plasmon nanostructures; ultraviolet; zinc oxide nanoparticles.