Welding tools of different designs have been used to join friction stir welding 2-mm-thick Al 7075 sheets, to investigate the effect of the tool geometry on the weld performance. Five cylindrical tools with different pin geometries were manufactured from heat-treatable low alloy steel WNr 1.6582/DIN 34CrNiMo6. Additionally, the effect of the welding speed was considered in the work, with six different speeds ranging from 80 mm/min to 300 mm/min. The weld tool rotational speed was kept constant at 1000 rpm and all other parameters were also kept constant in the experiments. The tensile strength was measured to investigate the mechanical properties of the weld. Results were processed with statistical analysis tools, which showed that the mechanical strength was affected by tool geometry as well as welding speed. The weld tool with the highest pin diameter achieved the highest tensile strength. The welding speed affected the tensile strength differently in the different weld tool geometries studied. The highest weld efficiency reported in the tests is 72.20%, achieved with a cylindrical pin weld tool at 250 mm/min.
Keywords: aluminum Al 7075; friction stir welding (FSW); rotational speed; tensile strength; thin sheet; tool geometry; welding speed.