Soft magnetic composites (SMCs) need a stable matrix to apply heat treatments for enhancing their magnetic characteristics. A stable matrix can be offered by alumina, but the densification of the ferromagnetic particles covered by this oxide (by sintering) can be very difficult. This paper proposes a feasible synthesis route for obtaining alumina matrix SMCs. An Fe-Si-Al alloy with nominal composition Fe85Si9Al6 was obtained by mechanical alloying of elemental Fe, Si, and Al powders, and further, the as-milled powders were superficially oxidized by immersion in HCl solution. The oxide layer was composed of iron, silicon, and aluminum oxides, as the Fourier-transform infrared spectroscopy technique revealed. The Fe-Si-Al@oxide powder was densified by the spark plasma sintering technique-SPS. Upon sintering, a continuous matrix of oxide (mainly alumina) was formed by the reaction of the Fe-Si-Al powder coreswith their oxide layer. The main part of the composite compacts after sintering consisted of an Fe3Si-ordered phase dispersed in an oxide matrix. The DC and AC tests of magnetic composite compacts showed that upon increasing the sintering temperature, the density, magnetic induction, and magnetic permeability increased. The initial magnetic permeability was constant in the entire range of testing frequencies and the magnetic losses increased linearly. The stability of the magnetic characteristics in frequency is promising for developing further such types of magnetic composite.
Keywords: Sendust; reaction sintering; soft magnetic composite; spark plasma sintering; surface oxidized powder.