The evolution of a nanostructured state of palladium-lead membrane alloys during their interaction with hydrogen was studied using precision X-ray diffraction with synchrotron radiation (SR) and scanning electron microscopy (SEM) with energy-dispersive X-ray spectroscopy (EDXS). The importance of this topic is due to the need and demand for improving the performance characteristics of dense metal diffusion filters for high purity hydrogen separation processes. Palladium-based membrane filters with lead concentrations of 5 and 20 wt.% were prepared via electric arc melting from high purity metals (99.95%). The thickness of the filters was 50 μm. Hydrogenation was carried out from a gas medium at 573 K and the pressure of 16 atm. within 150 min. The focus of the study is on the structural state of diffusion filter membranes depending on the content of the palladium-alloying element-lead-and on analysis of the substructure of alloys before and 5300 h relaxation after hydrogenation is carried out. Specific features of the surface morphology and the structure of the membrane filters depending on the concentration of lead in the alloys are determined. The formation and development of deformation processes in metal systems upon the hydrogenation is shown. The establishment of peculiarities of hydrogen interaction with metals will contribute to obtaining new potentially important characteristics of membrane filters.
Keywords: SEM-EDXS analysis; X-ray diffraction; hydrogen; palladium—lead membrane alloys.