SiO2 aerogels have attracted extensive attention due to their unique structural characteristics, which exhibit many special properties, especially good optical transparency. As far as we know, the sol-gel stage during the synthesis of aerogel plays an important role in the construction of the gel skeleton. In this study, we adjusted the amount of silicon source and catalyst to explore the best scheme for preparing highly transparent SiO2 aerogels, and further clarify the effects of both on the properties of SiO2 aerogels. Results indicated that the pore size distribution was between 10 and 20 nm, the thermal conductivity was between 0.0135 and 0.021 W/(m·K), and the transmittance reached 97.78% at 800 nm of the aerogels, better than most studies. Therefore, it has the potential to be used in aerogel glass for thermal insulation.
Keywords: SiO2 aerogels; high transparency; mesoporous materials; thermal insulation.