Purpose: The purpose of this in vitro study was to compare the flexural strength and Weibull characteristics of 3 different resin-ceramic materials with a zirconia-reinforced lithium silicate material after thermal-cycling.
Material and methods: Four different computer-aided design and computer-aided manufacturing restorative materials (Vita Enamic, Lava Ultimate, Crystal Ultra, and Vita Suprinity) were tested. A total of 40 Ø12×1.2-mm disks were prepared and divided into 4 groups (n = 10). Their flexural strength was evaluated after 5000 thermal-cycles with a 4-point biaxial flexure test using a universal testing machine. The Weibull modulus and probability of failure were also determined from the biaxial flexural strength data. Data were analyzed with one-way ANOVA and the Tukey pairwise comparison test (α = 0.05).
Results: Significant differences were found among the materials in terms of biaxial flexural strength (p < 0.05). Vita Suprinity had the highest mean ±standard deviation flexural strength (289.1 ± 15.1 MPa), and Vita Enamic had the lowest (100.0 ± 3.2 MPa). The highest Weibull modulus was calculated for Crystal Ultra, followed by Vita Enamic, Lava Ultimate, and Vita Suprinity.
Conclusion: Vita Suprinity had the highest flexural strength when compared with the other materials tested. Crystal Ultra had the highest flexural strength among the resin-ceramic materials. The highest Weibull modulus was calculated for Crystal Ultra and the lowest for Vita Suprinity.
Keywords: Flexural strength; Weibull modulus; resin ceramic; resin nanoceramics; zirconia-reinforced lithium silicate.
© 2022 by the American College of Prosthodontists.