This paper aims to explore the qualification of step- and lock-in heating thermography as techniques capable of inspecting new composite rail carbodies following input and inspection requirements set by the rail manufacturing industry. Specifically, we studied (a) a monolithic CFRP sample (20 mm thickness) and (b) a CFRP-PET foam-CFRP sandwich (40 mm total thickness) component, that were manufactured with artificial defects, to replicate the side wall sections of a carbody. The samples proved to be very challenging to test using only one-sided inspection due to (1) exhibiting significant thickness compared to existing literature, (2) low surface emissivity and (3) that the foam core of the sandwich sample was a thermal insulating material. In addition, the sandwich sample was designed with defects on both skins. Both thermography techniques provided similar defect detection results, although step heating offered faster detection. In the case of the monolithic panel, defects up to 10 mm depth were detected, with minor detection of defects at 15 mm depth with a step-heating protocol between 90 s and 120 s overall acquisition, which was faster than the 140 s used with the lock-in technique. For the sandwich component only the front skin defects were detected, with both techniques using heating protocols between 70-120 s.
Keywords: CF-PET-CF sandwich; IRT; NDE; NDT; composite rail carbodies; infrared thermography; lock-in heating; step heating; thermography.