In this work, we report on flexible toluene diisocyanate (TDI)-based polyurethane foams (FPUFs) chemically modified by POSS moieties, i.e., octa (3-hydroxy-3-methylbutyldimethylsiloxy) POSS (OCTA-POSS) and 1,2-propanediolizo-butyl POSS (PHI-POSS). The influence of silsesquioxane on the PU foaming process, structure, morphology, physicochemical, and mechanical properties, as well as flammability, was examined. FT-IR analysis provided evidence for the chemical incorporation of the nanofiller into the foam structure. It was found that the addition of POSS increases the apparent density of the foam and its compressive strength. The XRD and SEM-EDS techniques showed the uniform distribution of POSS in the FPUF with agglomeration depending on the kind and content of the introduced POSS moieties. The analysis of the thermogravimetric and microcalorimetry data revealed an improved resistance to the burning of FPUFs containing reactive POSS, as evidenced by the reduced rate of heat release (HRR). Importantly, the mechanical properties tests showed that the incorporation of silsesquioxane nanoparticles into the polyurethane structure via covalent bonds strengthens the foam integrity.
Keywords: POSS; flammability; flexible polyurethane foam; hybrid materials; oligosilsesquioxanes.