Single crystal diamond (SCD) is a promising material to satisfy emerging requirements of high-demand fields, such as microelectronics, beta batteries and wide-spectrum optical communication systems, due to its excellent optical characteristics, elevated breakdown voltage, high hardness and superior thermal conductivity. For such applications, it is essential to study the optically active defects in as-grown diamonds, namely three-dimensional defects (such as stacking faults and dislocations) and the inherent defects arising from the cultivation method. This paper reports the growth of SCD films on a commercial HPHT single-crystal diamond seed substrate using a 2.45 GHz microwave plasma-assisted chemical vapor deposition (MWPACVD) technique by varying the methane (CH4) gas concentration from 6 to 12%, keeping the other parameters constant. The influence of the CH4 concentration on the properties, such as structural quality, morphology and thickness, of the highly oriented SCD films in the crystalline plane (004) was investigated and compared with those on the diamond substrate surface. The SCD film thickness is dependent on the CH4 concentration, and a high growth rate of up to 27 µm/h can be reached. Raman spectroscopy, high-resolution X-ray diffractometry (HRXRD), scanning electron microscopy (SEM), surface profilometry and optical microscopic analyses showed that the produced homoepitaxial SCD films are of good quality with few macroscopic defects.
Keywords: defects; homoepitaxial growth; microwave plasma-assisted CVD; morphology; single crystal diamond.