Light and flexible electromagnetic-interference-shielding materials are of great significance to control electromagnetic pollution and protect the human body and other nearby equipment or systems. In this study, a film of polytetrafluoroethylene wrapped with copper (PTFE@Cu) was prepared by depositing Cu using electroless plating on the surface of a microporous PTFE film modified by dopamine. A Ni@PVDF membrane was fabricated by casting a suspension of Ni nanochains in PVDF. The two kinds of films were hot-pressed into an ultrathin and efficient electromagnetic-shielding film with a sandwich structure. PTFE and PVDF provided high flexibility to the composite film, while the metal-wrapped polymer fiber structure gave the film an excellent electromagnetic-shielding efficiency, and the Ni nanochains and laminated hot-pressing process further enhanced the shielding ability of the film. Through these combined effects, the conductivity of the composite film reached 1117.57 S cm-1 while the thickness was only about 80 μm, and the average shielding efficiency in the X-band range was as high as 57.16 dB with absorption accounting for about 67.2% of the total shielding. At the same time, the composite film had high strength and flexibility, and the tensile strength could reach 43.49 MPa. Even after bending 1000 times, the conductivity could still be maintained at 174.55 S cm-1, while the average shielding effectiveness in the X-band range was retained at 44.29 dB. The film has great latent applications in flexible devices and portable wearable intelligent devices.
This journal is © The Royal Society of Chemistry.