ZIF-67@ATP was prepared by the in situ growth of the zeolite imidazole frame (ZIF-67) on the surface of attapulgite (ATP). The structure and surface morphology of ZIF-67@ATP were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Different mass fractions of ATP and ZIF-67@ATP were added to ethylene vinyl acetate (EVA)/magnesium hydroxide (MH) composites as flame retardant synergists. The flame retardancy of EVA composites was evaluated by the limiting oxygen index (LOI) test, UL-94 test and cone calorimeter test. Composites containing 3 wt% of ZIF-67@ATP reached an LOI value of 43% and a V-0 rating in the UL-94 test, and the ignition time of the composite increased from 38 s to 56 s. The tensile strength and impact strength of the composites did not change significantly, but the elongation at break increased greatly. Typically, for composites containing 4 wt% of ZIF-67@ATP, the elongation at break of the composites increased from 69.5% to 522.2% compared to the samples without the synergist. This study provides novel insights into the application of attapulgite in the field of flame retardant polymer materials.
Keywords: EVA; ZIF-67; attapulgite; flame retardant; magnesium hydroxide.