Nanocomposite systems comprised of a poly(ethylene vinyl acetate) (EVA) matrix and carbon black (CB) or graphene nanoplatelets (GNPs) were used to investigate conductivity and crystallisation dynamics using a commercially relevant melt-state mixing process. Crystallisation kinetics and morphology, as investigated by DSC and SEM, turn out to depend on the interplay of (i) the interphase interactions between matrix and filler, and (ii) the degree of filler agglomeration. For the GNP-based systems, an almost constant conductivity value was observed for all compositions upon cooling, something not observed for the CB-based compositions. These conductivity changes reflect structural and morphological changes that can be associated with positive and negative thermal expansion coefficients. GNP-based systems were observed to exhibit a percolation threshold of approximately 2.2 vol%, lower than the 4.4 vol% observed for the CB-based systems.
Keywords: crystallisation dynamics; dielectric hysterisis; percolative networks.