The physicochemical and transport properties (ion-exchange capacity, water content, diffusion permeability, conductivity, and current-voltage characteristic) of a series of perfluorinated membranes with an inert fluoropolymer content from 0 to 40%, obtained by polymer solution casting, were studied. Based on the analysis of the parameters of the extended three-wire model, the effect of an inert component on the path of electric current flow in the membrane and its selectivity were estimated. The mechanical characteristics of the membranes, such as Young's modulus, yield strength, tensile strength, and relative elongation, were determined from the dynamometric curves. The optimal amount of the inert polymer in the perfluorinated membrane was found to be 20%, which does not significantly affect its structure and electrotransport properties but increases the elasticity of the obtained samples. Therefore, the perfluorinated membrane with 20% of inert fluoropolymer is promising for its application in redox flow batteries and direct methanol fuel cells.
Keywords: conductivity; current-voltage curve; diffusion permeability; direct methanol fuel cell; extended tree-wire model; inert fluoropolymer; perfluorinated membrane; redox flow battery; solution casting; stress-strain curve.