Energetic structural materials play an important role in improving the damage performance of future weapons. To improve the energy-releasing behavior, Al0.5NbZrTi1.5Ta0.8Cex high-entropy alloys were prepared by vacuum-arc melting. The results showed the presence of BCC and FCC phases in the alloy with dendritic-morphology-element segregation and there were significant dislocations in the alloys. The current study focused on the effects of cerium content on the dynamic compressive mechanical and energetic characteristics. Cerium doping enhanced the energy-releasing characteristics of high-entropy alloys. The severity of the reaction increased with the increase in the cerium content, while the dynamic compressive strength generally decreased with the increase in cerium content. The Al0.5NbZrTi1.5Ta0.8Ce0.25 showed excellent mechanical and energy-releasing characteristics. The ballistic experiments indicated that Al0.5NbZrTi1.5Ta0.8Ce0.25 can penetrate 6-millimeter A3 plates and ignite the cotton behind the target at a velocity of 729 m/s, making it an ideal energetic structural material.
Keywords: cerium doping; energy releasing; high-entropy alloys; mechanical behavior.