The aim of the presented study was to apply various bark species (birch, beech, maple, pine and spruce) as fillers for urea-formaldehyde (UF) resin in three-layer plywood manufacturing. For this purpose, all types of bark were ground and added to the adhesive mixture. The resultant plywood was subjected to investigations of the following: tensile strength, modulus of elasticity (MOE), bending strength (MOR) and formaldehyde emission. The results indicate a reduction in the tensile strength. Moreover, the lack of significant improvement in strength parameters can be explained by too high a load of the filler (20 wt%). In the case of formaldehyde emissions, a reduction was observed for birch (B-1), beech (B-2), maple (B-3) and pine bark (B-4). In addition, an increase in the emission of formaldehyde was recorded only for spruce bark.
Keywords: UF resin; bark; filler; formaldehyde emission; mechanical properties; plywood; wood-base materials.