Unlike fluorescence, room-temperature phosphorescence (RTP) has never been utilized to monitor the dynamic variation of polymer. In the present study, acrylate-vinylidene chloride (VDC) copolymers were doped with a good RTP molecule, N-hydroxyethyl 4-bromo-1,8-naphthalimide (HBN). During the maturation process, marked RTP-intensity enhancement of HBN was observed due to the crystallinity increase of copolymers, verified by X-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FTIR). For ensuring the more efficient RTP emission of HBN, copolymers with a higher content of crystallizable VDC segments and a more polar acrylate comonomer, i.e. methyl acrylate (MA) were preferred. According to the RTP characterizations, the following deductions could be obtained: (1) Maturation for 8-9 days at room temperature was needed for the copolymers with a high VDC content to ensure the complete crystallization; (2) Raising the maturation temperature to 50 and 70 °C not only accelerated the crystallization rate, but also increased the crystallinity of copolymers; (3) RTP method was more sensitive to the slight crystallinity variation than XRD and FTIR. Moreover, the dynamic maturation processes of acrylate-VDC copolymers could be also visually monitored through contacting with certain organic solvents that led to the emission color transition from orange to blue.
Keywords: Maturation; Monitoring; Room-temperature phosphorescence; Vinylidene chloride copolymers.
Copyright © 2022 Elsevier B.V. All rights reserved.